7/32” (5.69 mm) MONOCONDUCTOR CORROSION RESISTANT 1N22 MP35N

7/32” (5.69 mm) MONOCONDUCTOR, CORROSION RESISTANT 1N22 MP35N PROPERTIES

Cable Diameter	0.224” +0.005” - 0.002”	(5.69mm + 0.13mm -0.05mm)
Minimum Sheave Diameter	13”	(33 cm)
Cable Stretch Coeffcient	2.9 ft/Kft/Klbs	(3.30 m/Km/5KN)

7/32” (5.69 mm) MONOCONDUCTOR, CORROSION RESISTANT 1N22 MP35N ELECTRICAL

Maximum Conductor Voltage	1,200 VDC
Conductor AWG Rating	18
Minimum Insulation Resistance	1,500 Mega Ω/Kft @ 500VDC	(457 Mega Ω/Km @ 500VDC)
Armor Electrical Resistance	22.0 Ω/Kft	(72.2 Ω/Km)

7/32” (5.69 mm) MONOCONDUCTOR, CORROSION RESISTANT 1N22 MP35N MECHANICAL

Cable Breaking Strength Ends Fixed	5,200 lbs	(23.0 KN) Nominal
Maximum Suggested Working Tension	2,600 lbs	(11.6 KN)
Number and Size of Wires
Inner Armor	12 x 0.0310”	(0.787 mm)
Outer Armor	18 x 0.0310”	(0.787 mm)
Average Wire Breaking Strength
Inner Armor	204 lbs	(0.91 KN)
Outer Armor	204 lbs	(0.91 KN)

Cable Type	Core Description							Cable Weight
	Temp Rating °F °C	Plastic Type	Insulation Thickness in mm	Copper Construction in mm	Res Typical Ω/Kft Ω/Km	Cap. Typical pf/ft pf/m	O.D. Each in mm	in Air	in H2O
								lbs/Kft Kg/Km
1N22SA-MP35N	See Below	PFA	0.0305 0.078	7X0.0159 7X0.404	6.7 22.0	43 141	0.108 2.743	100 149	86 128

Insulation is rated to 500°F. Armor wires are rated to 475°F at 100% levels of H2S + CO2.
The armor wires are made of UNS R30035 (MP35N), a nickel-cobalt corrosion resistant alloy steel. Wires are preformed.
The nickel coated copper wires are made of ASTMB355 Class 10 and they are used to increase corrosion protection. Core
assembly – Copper strand consists of six wires around one center wire. Conductor resistance is measured at 68° F. Voids in
the copper strand are flled with a water-blocking agent to reduce water and gas migration.
SUPERSEAL, a special pressure seal agent, is applied between armor layers.
The temperature rating assumes a normal gradient for both temperature and weight.
All values shown are nominal or typical values.